點擊圖片查看大圖| NBR橡膠顆粒——注塑級物性參數 | |||||
| 性能 | 測試條件 | 典形數據 | 單位 | 測試方法 | 備注 |
| Properties | Test Condition | Typical value | Unit | Test Method | |
| 熔融流動速度 | 190℃/2.16Kg | 3.2 | g/10min | ASTM D1238 | |
| Melt Flow Rate | |||||
| 比重 | 25℃ | 0.96 | NA | ASTM D792 | |
| Specific Gravity | |||||
| 邵氏硬度 A | 25℃/5 Sec. | 54 | A | ASTM D2240 | |
| Shore Hardness A | |||||
| 拉伸強度 | 25℃/500 mm/min | 3.71 | Mpa | ASTM D412 | |
| Tensile Strength | |||||
| 延伸率 | 25℃/500 mm/min | 393 | % | ASTM D412 | |
| Ultimate Elongation | |||||
| 拉伸應力 | 25℃/500 mm/min | 2.93 | Mpa | ASTM D412 | |
| Tensile Stress @ | |||||
| 撕裂強度 | 25℃/500 mm/min | 10.09 | N/mm | ASTM D624 | |
| Tear Strength | |||||
| 壓縮變形 | 70℃/22Hrs | 41 | % | ASTM D395 B | |
| Compression Set | |||||
| 干燥條件/Drying Condition | |||||
| 80℃ -100℃ /2-4小時Hrs | |||||
| 工藝參數/Processing Conditions | |||||
| 機筒溫度 | 料筒前段 | 料筒中段 | 料筒后段 | 料筒噴嘴 | |
| Barrel temperature | Front section | Middle section | Rear section | Nozzle | |
| 溫度 | 180℃-190℃ | 190℃-210℃ | 190℃-210℃ | 180℃-190℃ | |
| Temperature | |||||
| *以上數據和資料僅作參考之用。所有數據是由我方實驗所得的真實數據并相信其準確性.不過,以上數據和資料不能保證可引伸至使用者,使用者應自行測試加以確認。 | |||||
| *The data & information here are for reference only. All data were generated in our laboratory and are true and trustable. However, these would not be guaranteed as sales specifications and the user should evaluate the suitability to their final applications. | |||||
溫馨提示您:
因塑膠原料行情每天每時波動較大無法及時更新，導致頁面上報價可能會與當天實際報價有所差異，請親們理解及時來電咨詢！
電話：鄧行秀女士0769-33327260或15817520076
公司：東莞市勝浩塑膠原料有限公司（樟木頭恒泰塑膠經營部）
地址：東莞市樟木頭鎮(zhèn)先威大道塑膠商務中心7棟56號
免責聲明：（1）以上所展示的信息由企業(yè)自行提供，內容的真實性、準確性和合法性由發(fā)布企業(yè)負責，環(huán)球塑化網對此不承擔任何保證責任。我們原則上建議您優(yōu)先選擇“塑企通”會員合作! （2）同時我們鄭重提醒各位買/賣家，交易前請詳細核實對方身份，切勿隨意打款或發(fā)貨，謹防上當受騙。如發(fā)現(xiàn)虛假信息，請向環(huán)球塑化網舉報。
簡繁切換