性能項(xiàng)目 |
試驗(yàn)條件[狀態(tài)] |
測試方法 |
測試數(shù)據(jù) |
數(shù)據(jù)單位 |
|
|
基本性能 |
吸水率 |
24小時浸漬(23℃) |
ASTM D-570 |
0.7 |
% |
|
吸水率 |
飽和(23℃) |
ASTM D-570 |
5.4 |
% |
|
|
物理性能 |
比重 |
|
ASTM D-792 |
1.38 |
|
|
機(jī)械性能 |
洛氏硬度M |
DAM |
ASTM D-785 |
M101 |
|
|
拉伸強(qiáng)度 |
23℃,DAM |
ASTM D-638 |
196.1 |
MPa |
|
|
埃佐沖擊強(qiáng)度 |
23℃,50%RH |
ASTM D-256 |
133 |
j/m |
|
|
埃佐沖擊強(qiáng)度 |
23℃,DAM |
ASTM D-256 |
107 |
j/m |
|
|
斷裂伸長率 |
23℃,DAM |
ASTM D-638 |
3 |
% |
|
|
撓曲模量 |
23℃,50%RH |
ASTM D-790 |
6205 |
MPa |
|
|
擠剪強(qiáng)度 |
23℃,DAM |
ASTM D-732 |
86 |
MPa |
|
|
撓曲模量 |
23℃,DAM |
ASTM D-790 |
8963 |
|
|
|
撓曲強(qiáng)度 |
23℃,DAM |
ASTM D-790 |
262 |
MPa |
|
|
拉伸強(qiáng)度 |
23℃,50%RH |
ASTM D-638 |
124.1 |
MPa |
|
|
泰伯磨耗量 |
50%RH |
|
14 |
cycles |
|
|
斷裂伸長率 |
23℃,50%RH |
ASTM D-638 |
4 |
% |
|
|
電氣性能 |
介電強(qiáng)度 |
DAM |
ASTM D-149 |
530 |
volts/mil |
|
介電強(qiáng)度 |
(分步法) |
ASTM D-149 |
440 |
volts/mil |
|
|
體積電阻率 |
RH |
ASTM D-257 |
109 |
ohm-cm |
|
|
體積電阻率 |
DAM |
ASTM D-257 |
1015 |
ohm-cm |
|
|
介電常數(shù) |
DAM@103Hz赫 |
ASTM D-150 |
4.5 |
|
|
|
介電常數(shù) |
RH@106Hz赫 |
ASTM D-150 |
10.7 |
|
|
|
損耗因數(shù) |
DAM@103Hz赫 |
ASTM D-150 |
0.02 |
|
|
|
介電常數(shù) |
RH@103Hz赫 |
ASTM D-150 |
25.0 |
|
|
|
損耗因數(shù) |
RH@106Hz赫 |
ASTM D-150 |
0.02 |
|
|
|
介電常數(shù) |
DAM@106Hz赫 |
ASTM D-150 |
3.7 |
|
|
|
熱性能 |
熱畸變溫度 |
1.8MPa |
ASTM D-648 |
249 |
℃ |
|
線性熱膨脹系數(shù) |
|
ASTM D-696 |
2.3×10-5 |
m/m/℃ |
|
|
熔點(diǎn) |
DAM |
ASTM D-789 |
255 |
℃ |
|
|
熔點(diǎn) |
50%RH |
ASTM D-789 |
255 |
℃ |
|