沙伯基礎創(chuàng)新塑料 聚丁烯對二酸酯PBT VALOX HX420HP
發(fā)布時間：2016-04-19 瀏覽次數：250 返回列表
|
|
|
Medium Flow, 30% Glass filled, Polybutylene Terephthalate (PBT) resin. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food contact compliant. Available in limited colors.
|
|
|
|
TYPICAL PROPERTIES (1)
|
|
MECHANICAL
|
Value
|
Unit
|
Standard
|
|
Tensile Stress, yld, Type I, 5 mm/min
|
1220
|
kgf/cm2
|
ASTM D 638
|
|
Tensile Stress, brk, Type I, 5 mm/min
|
1220
|
kgf/cm2
|
ASTM D 638
|
|
Tensile Strain, yld, Type I, 5 mm/min
|
3
|
%
|
ASTM D 638
|
|
Tensile Strain, brk, Type I, 5 mm/min
|
3
|
%
|
ASTM D 638
|
|
Tensile Modulus, 5 mm/min
|
94800
|
kgf/cm2
|
ASTM D 638
|
|
Flexural Stress, brk, 1.3 mm/min, 50 mm span
|
1920
|
kgf/cm2
|
ASTM D 790
|
|
Flexural Modulus, 1.3 mm/min, 50 mm span
|
77300
|
kgf/cm2
|
ASTM D 790
|
|
Hardness, Rockwell R
|
118
|
-
|
ASTM D 785
|
|
Tensile Stress, yield, 5 mm/min
|
125
|
MPa
|
ISO 527
|
|
Tensile Stress, break, 5 mm/min
|
125
|
MPa
|
ISO 527
|
|
Tensile Strain, yield, 5 mm/min
|
2
|
%
|
ISO 527
|
|
Tensile Strain, break, 5 mm/min
|
2
|
%
|
ISO 527
|
|
Tensile Modulus, 1 mm/min
|
9300
|
MPa
|
ISO 527
|
|
Flexural Stress, yield, 2 mm/min
|
195
|
MPa
|
ISO 178
|
|
Flexural Modulus, 2 mm/min
|
8500
|
MPa
|
ISO 178
|
|
IMPACT
|
Value
|
Unit
|
Standard
|
|
Izod Impact, unnotched, 23°C
|
81
|
cm-kgf/cm
|
ASTM D 4812
|
|
Izod Impact, notched, 23°C
|
8
|
cm-kgf/cm
|
ASTM D 256
|
|
Izod Impact, notched, -30°C
|
8
|
cm-kgf/cm
|
ASTM D 256
|
|
Instrumented Impact Total Energy, 23°C
|
101
|
cm-kgf
|
ASTM D 3763
|
|
Izod Impact, unnotched 80*10*4 +23°C
|
45
|
kJ/m2
|
ISO 180/1U
|
|
Izod Impact, unnotched 80*10*4 -30°C
|
45
|
kJ/m2
|
ISO 180/1U
|
|
Izod Impact, notched 80*10*4 +23°C
|
8
|
kJ/m2
|
ISO 180/1A
|
|
Izod Impact, notched 80*10*4 -30°C
|
7
|
kJ/m2
|
ISO 180/1A
|
|
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm
|
5
|
kJ/m2
|
ISO 179/1eA
|
|
THERMAL
|
Value
|
Unit
|
Standard
|
|
Vicat Softening Temp, Rate B/50
|
215
|
°C
|
ASTM D 1525
|
|
HDT, 0.45 MPa, 6.4 mm, unannealed
|
215
|
°C
|
ASTM D 648
|
|
HDT, 1.82 MPa, 6.4 mm, unannealed
|
207
|
°C
|
ASTM D 648
|
|
CTE, -40°C to 40°C, flow
|
2.52E-05
|
1/°C
|
ASTM E 831
|
|
CTE, 60°C to 138°C, flow
|
2.52E-05
|
1/°C
|
ASTM E 831
|
|
CTE, -40°C to 40°C, flow
|
2.5E-05
|
1/°C
|
ISO 11359-2
|
|
CTE, -40°C to 40°C, xflow
|
1.2E-04
|
1/°C
|
ISO 11359-2
|
|
Vicat Softening Temp, Rate B/50
|
215
|
°C
|
ISO 306
|
|
Vicat Softening Temp, Rate B/120
|
220
|
°C
|
ISO 306
|
|
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm
|
200
|
°C
|
ISO 75/Af
|
|
PHYSICAL
|
Value
|
Unit
|
Standard
|
|
Specific Gravity
|
1.53
|
-
|
ASTM D 792
|
|
Specific Volume
|
0.66
|
cm3/g
|
ASTM D 792
|
|
Water Absorption, 24 hours
|
0.06
|
%
|
ASTM D 570
|
|
Mold Shrinkage, flow, 3.2 mm (5)
|
0.3 - 0.8
|
%
|
SABIC Method
|
|
Mold Shrinkage, flow, 1.5-3.2 mm (5)
|
0.3 - 0.5
|
%
|
SABIC Method
|
|
Mold Shrinkage, flow, 3.2-4.6 mm (5)
|
0.5 - 0.8
|
%
|
SABIC Method
|
|
Mold Shrinkage, xflow, 1.5-3.2 mm (5)
|
0.4 - 0.6
|
%
|
SABIC Method
|
|
Mold Shrinkage, xflow, 3.2-4.6 mm (5)
|
0.6 - 0.9
|
%
|
SABIC Method
|
|
Melt Flow Rate, 250°C/2.16 kgf
|
17
|
g/10 min
|
ASTM D 1238
|
|
Density
|
1.53
|
g/cm3
|
ISO 1183
|
|
Water Absorption, (23°C/sat)
|
0.26
|
%
|
ISO 62
|
|
Moisture Absorption (23°C / 50% RH)
|
0.06
|
%
|
ISO 62
|
|
Melt Volume Rate, MVR at 250°C/2.16 kg
|
13
|
cm3/10 min
|
ISO 1133
|
|
ELECTRICAL
|
Value
|
Unit
|
Standard
|
|
Volume Resistivity
|
>3.2E+16
|
Ohm-cm
|
ASTM D 257
|
|
Dielectric Strength, in air, 3.2 mm
|
18.7
|
kV/mm
|
ASTM D 149
|
|
Dielectric Strength, in oil, 1.6 mm
|
24.8
|
kV/mm
|
ASTM D 149
|
|
Relative Permittivity, 100 Hz
|
3.8
|
-
|
ASTM D 150
|
|
Relative Permittivity, 1 MHz
|
3.7
|
-
|
ASTM D 150
|
|
Dissipation Factor, 100 Hz
|
0.002
|
-
|
ASTM D 150
|
|
Dissipation Factor, 1 MHz
|
0.02
|
-
|
ASTM D 150
|
|
Source GMD, last updated:2016/02/26
|
|
Parameter
|
|
Injection Molding
|
Value
|
Unit
|
|
Drying Temperature
|
120
|
°C
|
|
Drying Time
|
3 - 4
|
hrs
|
|
Drying Time (Cumulative)
|
12
|
hrs
|
|
Maximum Moisture Content
|
0.02
|
%
|
|
Melt Temperature
|
250 - 265
|
°C
|
|
Nozzle Temperature
|
245 - 260
|
°C
|
|
Front - Zone 3 Temperature
|
250 - 265
|
°C
|
|
Middle - Zone 2 Temperature
|
245 - 260
|
°C
|
|
Rear - Zone 1 Temperature
|
240 - 255
|
°C
|
|
Mold Temperature
|
65 - 90
|
°C
|
|
Back Pressure
|
0.3 - 0.7
|
MPa
|
|
Screw Speed
|
50 - 80
|
rpm
|
|
Shot to Cylinder Size
|
40 - 80
|
%
|
|
Vent Depth
|
0.025 - 0.038
|
mm
|
|
Source GMD, last updated:2016/02/26
|
|
|
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
|
|
|
PLEASE CONTACT US FOR AVAILABILITY IN YOUR REGION.
轉載請注明：轉載自環(huán)球塑化資訊網 http://www.42249.cn/news/
本文鏈接：http://www.42249.cn/b-shabo/news269598/
免責聲明：本文"沙伯基礎創(chuàng)新塑料 聚丁烯對二酸酯PBT VALOX HX420HP"僅代表作者個人觀點，與環(huán)球塑化網無關。環(huán)球塑化網所轉載的內容，其版權均由原作者和資料提供方所擁有！如因作品版權問題需要處理，請與我們聯絡。電話：400-115-2868
|
簡繁切換